COL ICSD Collection Code 1440 DATE Recorded Sep 10, 1984 NAME Silicon oxide MINR Tridymite - from Plumas county, California FORM Si O2 = O2 Si TITL The crystal structure of low tridymite REF Acta Crystallographica B (24,1968-38,1982) ACBCA 34 (1978) 391-403 AUT Konnert J H, ApplemanÿDÿE CELL a=9.932 b=17.216 c=81.864 à=90.0 á=90.0 ç=90.0 V=13997.9 Z=320 SGR F 1 (1) - triclinic CLAS 1 (Hermann-Mauguin) - C1 (Schoenflies) PARM Atom__No OxStat Wyck ---X--- ---Y--- ---Z--- -SOF- Si 1 4.000 4* 0.06049 0.03633 0.03414 Si 2 4.000 4* 0.56126 0.03679 0.03371 Si 3 4.000 4* -0.02022 0.19793 0.01846 Si 4 4.000 4* 0.23025 0.28978 0.02831 Si 5 4.000 4* 0.48204 0.19712 0.01779 Si 6 4.000 4* 0.72606 0.29128 0.02822 Si 7 4.000 4* 0.31136 0.46063 0.01895 Si 8 4.000 4* 0.81084 0.46158 0.01933 Si 9 4.000 4* 0.013 0.05235 0.07211 Si 10 4.000 4* 0.48576 0.03038 0.07135 Si 11 4.000 4* -0.01645 0.22688 0.0796 Si 12 4.000 4* 0.2307 0.31107 0.06598 Si 13 4.000 4* 0.4608 0.20317 0.07936 Si 14 4.000 4* 0.71072 0.28419 0.06598 Si 15 4.000 4* 0.25859 0.46761 0.08318 Si 16 4.000 4* 0.73949 0.44146 0.0834 Si 17 4.000 4* 0.05429 0.04643 0.12921 Si 18 4.000 4* 0.55652 0.04513 0.12951 Si 19 4.000 4* -0.02557 0.21178 0.11701 Si 20 4.000 4* 0.22884 0.2838 0.1327 Si 21 4.000 4* 0.48158 0.21099 0.11717 Si 22 4.000 4* 0.72795 0.28732 0.13375 Si 23 4.000 4* 0.30672 0.45008 0.12047 Si 24 4.000 4* 0.80469 0.45095 0.12077 Si 25 4.000 4* -0.00806 0.05747 1/6 Si 26 4.000 4* 0.51258 0.03123 1/6 Si 27 4.000 4* -0.03431 0.2153 0.18369 Si 28 4.000 4* 0.24039 0.27072 0.17021 Si 29 4.000 4* 0.48592 0.18696 0.18403 Si 30 4.000 4* 0.71198 0.29733 0.1714 Si 31 4.000 4* 0.2663 0.44539 0.1777 Si 32 4.000 4* 0.73858 0.47061 0.17894 Si 33 4.000 4* 0.04792 0.0354 0.23125 Si 34 4.000 4* 0.54997 0.03394 0.2318 Si 35 4.000 4* -0.03233 0.20609 0.22157 Si 36 4.000 4* 0.22078 0.30081 0.23164 Si 37 4.000 4* 0.46402 0.2026 0.22158 Si 38 4.000 4* 0.71696 0.29734 0.23155 Si 39 4.000 4* 0.297 0.46113 0.21579 Si 40 4.000 4* 0.79829 0.45915 0.21663 Si 41 4.000 4* -0.005 0.03156 0.26833 Si 42 4.000 4* 0.4936 0.02861 0.26878 Si 43 4.000 4* -0.07624 0.20251 0.27784 Si 44 4.000 4* 0.17311 0.29695 0.26892 Si 45 4.000 4* 0.42106 0.20037 0.2781 Si 46 4.000 4* 0.67164 0.2942 0.26879 Si 47 4.000 4* 0.2431 0.457 0.28464 Si 48 4.000 4* 0.74099 0.45386 0.28401 Si 49 4.000 4* -0.01127 0.05741 1/3 Si 50 4.000 4* 0.51099 0.03461 0.33274 Si 51 4.000 4* -0.03549 0.21523 0.31602 Si 52 4.000 4* 0.23592 0.27164 0.33012 Si 53 4.000 4* 0.48141 0.19216 0.31597 Si 54 4.000 4* 0.71254 0.29525 0.3294 Si 55 4.000 4* 0.26507 0.44681 0.32239 Si 56 4.000 4* 0.73711 0.46883 0.32151 Si 57 4.000 4* 0.05402 0.04624 0.37071 Si 58 4.000 4* 0.55433 0.04489 0.37002 Si 59 4.000 4* -0.02367 0.20997 0.38348 Si 60 4.000 4* 0.22606 0.28414 0.36728 Si 61 4.000 4* 0.47769 0.20929 0.3829 Si 62 4.000 4* 0.72917 0.28317 0.36679 Si 63 4.000 4* 0.30406 0.44985 0.37919 Si 64 4.000 4* 0.80457 0.44962 0.37903 Si 65 4.000 4* 0.01089 0.04822 0.42801 Si 66 4.000 4* 0.49177 0.02779 0.42869 Si 67 4.000 4* -0.01648 0.22402 0.42095 Si 68 4.000 4* 0.23522 0.3033 0.43401 Si 69 4.000 4* 0.46602 0.20096 0.4208 Si 70 4.000 4* 0.71384 0.28565 0.43382 Si 71 4.000 4* 0.26175 0.45878 0.41648 Si 72 4.000 4* 0.74321 0.44246 0.41648 Si 73 4.000 4* 0.00089 0.03822 0.4658 Si 74 4.000 4* 0.50365 0.03917 0.46628 Si 75 4.000 4* -0.06794 0.19996 0.48037 Si 76 4.000 4* 0.18252 0.29559 0.47201 Si 77 4.000 4* 0.432 0.2 0.48127 Si 78 4.000 4* 0.6804 0.29548 0.47172 Si 79 4.000 4* 0.25501 0.46482 0.48221 Si 80 4.000 4* 0.75445 0.46519 0.48184 O 1 -2.000 4* 0.02331 0.0288 0.05321 O 2 -2.000 4* 0.53202 0.03557 0.05282 O 3 -2.000 4* 0.18855 0.3045 0.04704 O 4 -2.000 4* 0.68116 0.30149 0.04695 O 5 -2.000 4* -0.06621 0.2291 0.09828 O 6 -2.000 4* 0.4512 0.22872 0.09819 O 7 -2.000 4* 0.28736 0.43393 0.10126 O 8 -2.000 4* 0.78692 0.42769 0.10194 O 9 -2.000 4* 0.03987 0.06824 0.14807 O 10 -2.000 4* 0.53585 0.0651 0.14851 O 11 -2.000 4* 0.19016 0.26991 0.15158 O 12 -2.000 4* 0.69419 0.27038 0.15271 O 13 -2.000 4* -0.06233 0.19435 0.2025 O 14 -2.000 4* 0.43292 0.1879 0.20259 O 15 -2.000 4* 0.27472 0.47082 0.19647 O 16 -2.000 4* 0.79075 0.46998 0.19732 O 17 -2.000 4* 0.03607 0.0089 1/4 O 18 -2.000 4* 0.54753 0.00924 0.25073 O 19 -2.000 4* 0.20233 0.32513 1/4 O 20 -2.000 4* 0.69557 0.32268 1/4 O 21 -2.000 4* -0.06081 0.19694 0.29712 O 22 -2.000 4* 0.4325 0.19703 0.29745 O 23 -2.000 4* 0.28913 0.46581 0.30342 O 24 -2.000 4* 0.78507 0.46136 0.30288 O 25 -2.000 4* 0.03549 0.07231 0.35209 O 26 -2.000 4* 0.54098 0.06541 0.35093 O 27 -2.000 4* 0.18331 0.26704 0.34864 O 28 -2.000 4* 0.69788 0.26518 0.34786 O 29 -2.000 4* -0.0656 0.22485 0.40227 O 30 -2.000 4* 0.44709 0.22556 0.402 O 31 -2.000 4* 0.28665 0.42878 0.39814 O 32 -2.000 4* 0.79172 0.43183 0.39803 O 33 -2.000 4* 0.02675 0.02229 0.44667 O 34 -2.000 4* 0.53965 0.02918 0.44729 O 35 -2.000 4* 0.19695 0.30664 0.45287 O 36 -2.000 4* 0.683 0.3092 0.45242 O 37 -2.000 4* -0.05068 0.17436 0.49912 O 38 -2.000 4* 0.45126 0.1723 1/2 O 39 -2.000 4* 0.28663 0.48885 0.50083 O 40 -2.000 4* 0.78581 0.48869 1/2 O 41 -2.000 4* -0.03453 -0.02233 0.02397 O 42 -2.000 4* 0.21504 0.01065 0.03152 O 43 -2.000 4* 0.46516 -0.02383 0.0244 O 44 -2.000 4* 0.71548 0.00966 0.03108 O 45 -2.000 4* 0.03828 1/8 0.02849 O 46 -2.000 4* 0.5435 0.12344 0.02711 O 47 -2.000 4* -0.15552 0.22774 0.02709 O 48 -2.000 4* 0.09752 0.26258 0.01843 O 49 -2.000 4* 0.3472 0.22544 0.02695 O 50 -2.000 4* 0.59632 0.26374 0.01782 O 51 -2.000 4* 0.28313 0.36924 0.02027 O 52 -2.000 4* 0.77913 0.37097 0.02058 O 53 -2.000 4* -0.13521 0.03536 0.0791 O 54 -2.000 4* 0.12074 0.00451 0.08279 O 55 -2.000 4* 0.36614 -0.03305 0.07245 O 56 -2.000 4* 0.60971 0.00404 0.08268 O 57 -2.000 4* 0.04317 0.14369 0.07451 O 58 -2.000 4* 0.42613 0.11183 0.07778 O 59 -2.000 4* -0.13907 0.25131 0.06786 O 60 -2.000 4* 0.10255 0.29035 0.07728 O 61 -2.000 4* 0.353 0.25204 0.06899 O 62 -2.000 4* 0.60949 0.21645 0.07209 O 63 -2.000 4* 0.27766 0.39862 0.07004 O 64 -2.000 4* 0.6808 0.36035 0.07652 O 65 -2.000 4* -0.03956 -0.02582 0.12417 O 66 -2.000 4* 0.208 0.02253 1/8 O 67 -2.000 4* 0.45867 -0.02388 0.12378 O 68 -2.000 4* 0.71016 0.01902 0.12657 O 69 -2.000 4* 0.01672 0.12187 0.11855 O 70 -2.000 4* 0.53102 0.12274 0.11909 O 71 -2.000 4* -0.15153 0.2302 0.12863 O 72 -2.000 4* 0.09963 0.26688 0.12146 O 73 -2.000 4* 0.34668 0.22426 0.12767 O 74 -2.000 4* 0.5967 0.27066 0.12288 O 75 -2.000 4* 0.27857 0.37158 0.13039 O 76 -2.000 4* 0.77435 0.37635 0.13196 O 77 -2.000 4* -1/8 -0.00657 0.16729 O 78 -2.000 4* 0.11944 0.03418 0.17769 O 79 -2.000 4* 0.36308 -0.00436 0.16748 O 80 -2.000 4* 0.6193 -0.03701 0.17025 O 81 -2.000 4* -0.06677 0.13958 0.17288 O 82 -2.000 4* 0.53602 0.10036 0.1796 O 83 -2.000 4* -0.13692 0.28276 0.17792 O 84 -2.000 4* 0.11713 0.24625 0.18189 O 85 -2.000 4* 0.36134 0.20851 0.1722 O 86 -2.000 4* 0.6079 0.24769 0.18233 O 87 -2.000 4* 0.29727 0.35425 0.17561 O 88 -2.000 4* 0.67902 0.38824 0.17331 O 89 -2.000 4* -0.04879 -0.01691 0.21988 O 90 -2.000 4* 0.20109 0.02038 0.2256 O 91 -2.000 4* 0.45224 -0.02256 0.22162 O 92 -2.000 4* 0.70138 0.02185 0.2252 O 93 -2.000 4* 0.0161 0.12601 0.22966 O 94 -2.000 4* 0.50938 0.1233 0.23024 O 95 -2.000 4* -0.16976 0.23072 0.23071 O 96 -2.000 4* 0.07875 0.27201 0.22448 O 97 -2.000 4* 0.32898 0.23136 0.23066 O 98 -2.000 4* 0.57759 0.26756 0.22387 O 99 -2.000 4* 0.26947 0.37294 0.2208 O 100 -2.000 4* 0.76357 0.37077 0.2209 O 101 -2.000 4* -0.13495 -0.01919 0.27293 O 102 -2.000 4* 0.11728 0.01166 0.2805 O 103 -2.000 4* 0.36767 -0.02723 0.27257 O 104 -2.000 4* 0.61405 0.01162 0.28149 O 105 -2.000 4* -0.04016 0.12214 0.26904 O 106 -2.000 4* 0.44879 0.1177 0.26981 O 107 -2.000 4* -0.23071 0.22311 0.27351 O 108 -2.000 4* 0.01841 0.26978 0.2703 O 109 -2.000 4* 0.26732 0.22413 0.27369 O 110 -2.000 4* 0.51778 0.26532 0.27027 O 111 -2.000 4* 0.20067 0.36812 0.28124 O 112 -2.000 4* 0.69288 0.36573 0.28107 O 113 -2.000 4* -0.1317 -0.00455 1/3 O 114 -2.000 4* 0.11483 0.03043 0.32267 O 115 -2.000 4* 0.36017 0.00074 0.33242 O 116 -2.000 4* 0.61297 -0.03472 0.32792 O 117 -2.000 4* -0.06702 0.13839 0.32644 O 118 -2.000 4* 0.53016 0.10446 0.31991 O 119 -2.000 4* -0.13852 0.28144 0.32215 O 120 -2.000 4* 0.11564 0.24608 0.31821 O 121 -2.000 4* 0.35817 0.21043 0.3281 O 122 -2.000 4* 0.60566 1/4 0.31821 O 123 -2.000 4* 0.29305 0.35586 0.32543 O 124 -2.000 4* 0.68387 0.38747 0.32871 O 125 -2.000 4* -0.0427 -0.02487 0.37553 O 126 -2.000 4* 0.20763 0.01843 0.37297 O 127 -2.000 4* 0.45804 -0.02593 3/8 O 128 -2.000 4* 0.70792 0.01982 0.37353 O 129 -2.000 4* 0.0251 0.1208 0.38207 O 130 -2.000 4* 0.52151 0.12008 0.38091 O 131 -2.000 4* -0.15424 0.22357 0.37223 O 132 -2.000 4* 0.0963 0.26815 0.37864 O 133 -2.000 4* 0.34475 0.22541 0.37221 O 134 -2.000 4* 0.59553 0.26715 0.3773 O 135 -2.000 4* 0.27131 0.37337 0.3686 O 136 -2.000 4* 0.77472 0.37183 0.36876 O 137 -2.000 4* -0.13518 0.02894 0.42062 O 138 -2.000 4* 1/8 0.00585 0.41725 O 139 -2.000 4* 0.37026 -0.03506 0.42775 O 140 -2.000 4* 0.6125 -0.00547 0.41758 O 141 -2.000 4* 0.03729 0.14034 0.42652 O 142 -2.000 4* 0.43439 0.1091 0.42224 O 143 -2.000 4* -0.1345 0.25449 0.43264 O 144 -2.000 4* 0.10837 0.28407 0.42256 O 145 -2.000 4* 0.35841 0.24435 0.43203 O 146 -2.000 4* 0.6145 0.21651 0.42794 O 147 -2.000 4* 0.28704 0.38952 0.42918 O 148 -2.000 4* 0.68536 0.3596 0.42246 O 149 -2.000 4* -0.11012 -0.02326 0.47172 O 150 -2.000 4* 0.13973 0.02249 0.47529 O 151 -2.000 4* 0.38978 -0.02228 0.47128 O 152 -2.000 4* 0.64061 0.02355 0.47609 O 153 -2.000 4* -0.04298 0.12673 0.46855 O 154 -2.000 4* 0.45817 0.12756 0.46933 O 155 -2.000 4* -0.22182 0.22704 0.47767 O 156 -2.000 4* 0.02843 0.27144 0.47573 O 157 -2.000 4* 0.27839 0.22882 0.47931 O 158 -2.000 4* 0.52864 0.27213 0.47694 O 159 -2.000 4* 0.20922 0.37595 0.48142 O 160 -2.000 4* 0.71419 3/8 0.48105 RVAL 0.064 TEST At least one temperature factor missing in the paper. (Code 53) TEST The lattice paramters are unusual but agree with the paper. (Code 55)